The beneficiation of mica ore is the enrichment process of raw mica. Raw mica refers to mica crystal of any thickness in the original ore with a contour area greater than or equal to 4 cm2. The amount of raw mica in raw ore is called the raw mica mineralization rate, which is usually expressed by the weight of raw mica contained in the unit ore volume (kg/m3). The ratio of the total weight of raw mica in the concentrate obtained from the ore dressing to the total weight of the raw mica contained in the ore is called the recovery rate. The industry mainly uses mica natural crystals directly to process the desired products. The larger the mica crystal without defects, the higher its economic value. Therefore, in the process of beneficiation of mica ore, it is necessary to protect the natural crystals of mica from damage as much as possible. At present, the beneficiation of mica with crystal contour area greater than 4 cm2 is mainly based on the difference in shape and friction coefficient between mica crystal and gangue. The commonly used methods are hand selection, friction selection and shape selection. For the crushed mica with a crystal contour area of ​​less than 4 cm2, it is mainly sorted according to the difference between its physical and chemical properties on the surface of the gangue. The method used is flotation. Mica seed dressing method and process a, hand selection Workers select the mica that has been separated by monomer on the mining face or the pit ore heap; the mica and the gangue are broken by hand hammer, and then the mica is selected. b, friction dressing The mica crystal and the gangue are separated according to the difference between the sliding friction coefficient of the slab-shaped mica crystal and the rolling friction coefficient of the spheroidal gangue. One of the devices used is a swash plate sorter. The machine is composed of a group of metals consisting of the swash plate, the swash plate of each length of 1350mm, width of 1000mm, under an angle larger than the inclination of the swash plate on a swash plate. A slit for collecting mica crystals is left at the lower end of each swash plate, and the width thereof is sequentially decreased in the order of slanting plates. The front edge of the slit is equipped with a triangular raft. During the sorting process, the large gangue rolls down to the stone pile; the mica and the smaller gangue block are blocked by the raft, and the sloping plate is dropped through the gap. The above process is repeated on the swash plate in turn to gradually separate the mica from the gangue. At present, the friction beneficiation process and equipment are not perfect, so this method has not been widely used in mica ore dressing. C, shape dressing According to the shape of the mica crystal and the gangue, the ability to pass through the sieve slit and the sieve hole in the sieve is different, and the mica and the gangue are separated. When sorting, a sieve having two or more different sieve surface structures is used, generally the first sieve mesh is strip-shaped; the second sieve mesh is square. When the ore enters the sieve surface, due to vibration or rolling action, the flaky mica and small gangue can leak from the strip sieve to the second sieve; because the second layer is sieve, the gangue can be sieved. Lower flaky mica. The shape beneficiation method has the advantages of simple process, less equipment, high productivity, good sorting effect, etc., and thus has been widely used in mica mines. The beneficiation of mica ore is the enrichment process of raw mica. Raw mica refers to mica crystal of any thickness in the original ore with a contour area greater than or equal to 4 cm2. The amount of raw mica in raw ore is called the raw mica mineralization rate, which is usually expressed by the weight of raw mica contained in the unit ore volume (kg/m3). The ratio of the total weight of raw mica in the concentrate obtained from the ore dressing to the total weight of the raw mica contained in the ore is called the recovery rate. The industry mainly uses mica natural crystals directly to process the desired products. The larger the mica crystal without defects, the higher its economic value. Therefore, in the process of beneficiation of mica ore, it is necessary to protect the natural crystals of mica from damage as much as possible. At present, the beneficiation of mica with crystal contour area greater than 4 cm2 is mainly based on the difference in shape and friction coefficient between mica crystal and gangue. The commonly used methods are hand selection, friction selection and shape selection. For the crushed mica with a crystal contour area of ​​less than 4 cm2, it is mainly sorted according to the difference between its physical and chemical properties on the surface of the gangue. The method used is flotation. Mica seed dressing method and process a, hand selection Workers select the mica that has been separated by monomer on the mining face or the pit ore heap; the mica and the gangue are broken by hand hammer, and then the mica is selected. b, friction dressing The mica crystal and the gangue are separated according to the difference between the sliding friction coefficient of the slab-shaped mica crystal and the rolling friction coefficient of the spheroidal gangue. One of the devices used is a swash plate sorter. The machine is composed of a set of metal slanting plates, each of which has a length of 1350 mm and a width of 1000 mm, and the inclination angle of the next inclined plate is greater than the inclination of the upper inclined plate. A slit for collecting mica crystals is left at the lower end of each swash plate, and the width thereof is sequentially decreased in the order of slanting plates. The front edge of the slit is equipped with a triangular raft. During the sorting process, the large gangue rolls down to the stone pile; the mica and the smaller gangue block are blocked by the raft, and the sloping plate is dropped through the gap. The above process is repeated on the swash plate in turn to gradually separate the mica from the gangue. At present, the friction beneficiation process and equipment are not perfect, so this method has not been widely used in mica ore dressing. C, shape dressing According to the shape of the mica crystal and the gangue, the ability to pass through the sieve slit and the sieve hole in the sieve is different, and the mica and the gangue are separated. When sorting, a sieve having two or more different sieve surface structures is used, generally the first sieve mesh is strip-shaped; the second sieve mesh is square. When the ore enters the sieve surface, due to vibration or rolling action, the flaky mica and small gangue can leak from the strip sieve to the second sieve; because the second layer is sieve, the gangue can be sieved. Lower flaky mica. The shape beneficiation method has the advantages of simple process, less equipment, high productivity, good sorting effect, etc., and thus has been widely used in mica mines. Sports Shoes For Women,Womens Tennis Shoes,Football Shoes For Women,Womens Basketball Shoes Shangqiu JIAYING SHOES CO.,LTD. , https://www.jiayingshoes.com