LCX-type high viscosity pump Roots pump sub-belt drive and gear reducer drive in two forms.This pump has: low speed, high efficiency, small size, large flow, low power consumption, self-absorption ability, Easy to use and so on.It can be widely used in conveying petroleum and petroleum products (gasoline exchangeable copper pump leaf) and various kinds of oils and liquids in the factory such as crude oil, paint, lubricating oil, glass glue, oleic acid, toothpaste and alkali (Soap processing) liquid, etc .; food processing can transport a variety of liquids, such as soy milk, yeast, syrup, etc .. Loading and unloading all kinds of tankers and tanker speed, high efficiency, easy to use, can be positive and negative work. More keyword search: Roots pump
Nickel Based Laser
Cladding Powder
Ni base alloy
powder is mainly made of NiCrBSi or NiBSi. Ni-based self-fluxing powder has
good wettability, corrosion resistance and high temperature self-lubricating
effect, and is used in components with heat resistance, corrosion resistance and
thermal fatigue resistance. In general Ni35,Ni45,Ni60 etc can be used for laser
cladding, the No means hardness of powder. Inconel 625 and 718 has good
corrosion property under higher temperature, also widely used for laser
cladding process.
Cobalt based Laser
Cladding Powder
Cobalt-based alloy
powder is the cemented carbide resistant to various types of wear and corrosion
as well as high temperature oxidation. That is, the so-called
cobalt-chromium-tungsten (molybdenum) alloy or Stellite alloy cobalt-based
alloy is mainly composed of cobalt, containing a considerable amount of nickel,
chromium, tungsten and a small amount of molybdenum, niobium, tantalum,
titanium, Alloying elements such as lanthanum, and occasionally a class of
alloys containing iron.
Co-based self-fluxing
alloys have good high temperature performance and wear resistance and corrosion
resistance, and are used in petrochemical power, metallurgy and other
industrial fields where they are wear-resistant, corrosion-resistant and
high-temperature resistant.
Iron based Laser
Cladding Powder
The work pieces
required for laser cladding and manufacturing in the actual industry are mainly
carbon steel and cast steel. The Fe-based alloy is close to the base material
in composition and has good wettability. The advantage of Fe base powder is
lower cost and good wear resistant of cladding layer. As a result, it`s the
most widely used for laser cladding process. It is suitable for parts that
require local wear resistance and are easily deformed.
WC blended Laser
Cladding Powder
Tungsten carbide blended with Ni alloy powder is the best
choice for wear resistant work piece. This unique process can bring excellent
wear, corrosion and high temperature resistant. Our blend powder can achieve
different portion of WC from 35% to 60% without crack under suitable cladding
parameter.
Iron Alloy Powder,Nickel Alloy Powder,Cobalt Alloy Powder,Laser Cladding Powder Luoyang Golden Egret Geotools Co., Ltd , https://www.xtccarbide.com
1, always check the oil level position, do not meet the requirements must be adjusted to meet the requirements to Roots pump operation, the oil level to the oil standard shall prevail.
2, the oil change deadline according to the actual conditions of use and can meet the performance requirements and other considerations, the user discretion. General new Roots pump, pumping clean and dry gas, it is recommended to work about 100 hours oil change once. Can not see the black metal powder, the oil may be extended after the period.
3, regular inspection of oil quality, oil deterioration should be found in a timely manner to replace the new oil, to ensure Roots pump is working properly.
4, under normal circumstances, Roots pump work after 2000 hours should be overhauled to check the aging degree of plastic seal, check whether the exhaust valve cracking, cleaning the valve plate and exhaust valve seat on the dirt cleaning the entire Roots pump cavity components, such as the rotor, rotary blades, springs, etc .. General gasoline wash, and drying. After the rubber parts dry with a dry cloth can be. hurt.
5, add bearing lubricating oil to the bearing body, observe the oil level should be at the center line of the oil standard, the lubricating oil should be replaced or replenished in time.
6, check the Roots pump pipe and loose joints with the phenomenon of hand rotating Roots pump, see Roots pump is flexible.
7, should be reassembled after the trial operation, the general should be empty for 2 hours and oil change twice, due to cleaning in the Roots pump will leave a certain amount of volatile materials, to be functioning properly, then put into normal work.
8, start the motor, when Roots pump normal operation, open the outlet pressure gauge and import Roots pump, depending on the pressure showed its appropriate, and gradually open the gate valve, while checking the motor load conditions.
9, try to control the Roots pump flow and head of the range indicated on the sign to ensure the Roots pump at maximum efficiency point of operation, in order to get the maximum energy-saving effect.
10, Roots pump to stop using, first close the gate valve, pressure gauge, and then stop the motor.
11, Roots pump during operation, the bearing temperature can not exceed the ambient temperature 35C, the maximum temperature shall not exceed 80C.
12, Roots pump in the first month of work, after 100 hours to replace the oil, after each 500 hours, oil change time.
13, often adjust the packing gland, to ensure that the drip filling room is normal (as drops into leakage is appropriate).
14, check the wear and tear of the sleeve regularly, after wear and tear should be promptly replaced.
15, Roots pump long-term deactivation, the pump required to open all, dry the water, the rotating parts and joints coated with grease installed, safekeeping.
16, Roots pump when used in winter season, after parking, you need to unscrew the lower part of the drain plug to the media to release the net.